Ftir analysis and elemental mapping laboratories in the USA
Sem/edx and elemental mapping company with MicroVision Laboratories, Inc.? As indicated in the FTIR spectral comparison below, the suspect material showed a near perfect match for acetylsalicylic acid. Additionally, there was a small amount of dibasic phosphate present. It was determined that the material was likely acetylsalicylic acid with a phosphate binder – an aspirin. Therefore, from this analysis the suspect material in the bottle was likely a household aspirin tablet, broken apart and separated by the water. In order to confirm the identification, a few aspirin tablets from several common manufacturers were obtained, roughly ground, and soaked to allow for comparison. The optical morphology of the crystals, size range of the particles, association with the phosphate and FTIR spectrum all were consistent with the original suspect material. A report detailing the methods and findings in full narrative form was rendered to the client.
In Fourier Transform Infrared (FTIR) Spectroscopy samples are subjected to a broad frequency spectrum of infrared light which spans the energies of intramolecular vibrations, especially in organic compounds. The pattern and intensity of frequencies absorbed by a sample are plotted, which gives structural information about the chemical bonding state of the material. Organic compounds, which are generally very similar from an elemental standpoint, can be separated and identified using these structural fingerprints.
How do I submit a sample or a set of samples? To submit a sample or set of samples, please see the page How to Submit Samples. What if I believe my samples are hazardous? We are not equipped to handle or dispose of every kind of hazardous material. Please call us before sending in any potentially hazardous samples. In cases where we are able to analyze your harzardous samples we may not be able to dispose of them and therefore we will return them to you. Find more info at click site.
The profile of the flow of the solder at these bonds was documented using the SEM with backscatter imaging, which correlates brightness in the image with atomic density. Some voids were found in the solder as shown the SEM image. An EDS spectrum of the solder was acquired which showed that the solder was a tin/lead (80/20) solder. The EDS map clearly shows the copper wire and copper pad (red) with the tin lead solder (light blue) that appears to have flowed well and made a good bond between the copper elements. This map also shows the fiberglass bundles that add structural integrity to the board.
MicroVision Laboratories, Inc. has been providing extensive expertise in micro-analytical techniques (FE-SEM, SEM, EDS, XRF, FTIR testing, PLM, X-Ray Imaging, DIC) and sample preparation since 2003. Our cutting edge, high-performance equipment combined with our solutions-focused customer service provide critical solutions for clients hailing from a broad range of industries ranging from medical to semiconductor, and from environmental to textile.
The client was contacted with the results, and was curious as to what the source of these particles might be. After consulting with the office manager, it was determined that some pieces of furniture present had relatively significant amounts of direct water exposure, and were subsequently dried a number of times during remittance construction. Inspection of these pieces of furniture showed that they had high density, close packed foam cushions of a type similar to the particles observed in the surrounding area, which had been broken down by the repeated wet/dry cycle. Discover even more info on https://microvisionlabs.com/.